Product Details:
|
Material: | 100% Polypropylene | Density: | 0.91g/cm3 |
---|---|---|---|
Fiber Length: | 54mm | Tensile Strength: | 500 Mpa.min |
Elongation At Break: | 15-20% | Melting Point: | 160-170 |
Elastic Modulus: | 5000 Mpa.min | Ignition Points: | 160-170 |
Equivalent Dia(mm): | 0.3+-0.05 |
Specification:
Raw Material
|
PP/PE
|
Fiber Type
|
Twisted Bunchy form
|
Length (mm)
|
40/48/50/54
|
Diameter (mm)
|
0.3+/-0.05
|
Strength (Mpa)
|
>560
|
Elastic Modulus (Mpa)
|
>5000
|
Break tesile ratio (%)
|
>15
|
Density (g/cm3)
|
0.91
|
1. Ration design of the fiber concrete:
Generally the recommended amount to add to the concrete is more than 2.7kg per m3(volume ratio is 0.3%), reinforcement adding amount is 5.5kg, Compared with adding 47kg of steel fibre, 5.4kg polymer fiber has the same volume ratio to the concrete.
2. Length: 54mm for common crack-resistant requirement.
3. Matching Ratio: Usually, it is no need to Change the matching ratio of the concrete. Considering the requirement of fissure-resistant, the polymer fiber is recommend to combine with the PP fiber mesh form with the volume ratio of 1:1 (0.9kg fiber-mesh to per m3 of cement concrete).
4. Mixer Adoption: Double-axle horizontal compelling mixer is priority.
5. Mixing process: Crushed stones, fibers and sands are put into the mixer in succession. After stirring for two minutes, fiber will fully spread and then add cement and water and stir normally. The addition of materials also can be put into as common concrete, but the stirring time should be properly prolonged to make fiber completely mixed
6. Shaping & Maintenance: There is no special requirement, may along the vibrating time for 30s, The maintenance of the fiber concrete should be done same as the normal concrete.
1. concrete reinforcement
2. Industrial Floor