Product Details:
|
| Acid Value ( MgKOH/ G): | ≤ 5 | Solvent Viscosity* (mPa · S/25℃): | 150-450 |
|---|---|---|---|
| Melt Viscosity (mPa ·s/ 160℃): | 1500-8000 | Softening Point (℃): | 105-130 |
| Appearance: | Light Yellow Granular Transparent Solid | Feature: | Non- Toxic, No Irritant, Dissolve In Most Organic Solvents, Insoluble In Water |
| Application: | Mainly Used For Attire, Shoes, Leather, Electronic Devices | ||
| Highlight: | Transparent Solid Polyamide Adhesive,Polyamide Adhesive Light Yellow Granular,Polyamide Hot Melt Adhesive For Attire |
||
Light Yellow Granular Transparent Solid Polyamide Hot Melt Adhesive For Attire And Shoes
Instruction:
Polyamide Hot Melt Adhesive is the polycondensate of dimer acid and diamine. It is solid at room temperature, but liquid uner melting state with good liguidity and adhesive ability, and will form high strength adhesion after solidifying and cooling. Polyamide hot melt adhesive has excellent thermostability and flexibility, as well as good solubility & melting properties at low temperature.
| Appearance | light yellow granular transparent solid |
| Properties | non- toxic, no irritant, dissolve in most organic solvents, insoluble in water. polyamide hot melt adhesive has a good solubility at low temperature |
| Application | mainly used for attire, shoes, leather, electronic devices, melting adhesive. Also used for wood, plastic, metal, ceramics etc |
| Packing | kraft bag lined with plastic bag, 25kg/bag net |
| Storage | to be stored in cool, ventilated and dry place |
Specification:
| Item | Index | ||||
| BT-208A | BT-208B | BT-208C | BT-288 | BT-208E | |
| Acid value ( mgKOH/ g) | ≤ 5 | ≤ 5 | ≤ 5 | ≤ 5 | ≤ 6 |
| Amine value (mgKOH/ g) | ≤ 5 | ≤ 5 | ≤ 5 | ≤ 5 | ≤ 6 |
| Solvent viscosity* (mPa · s/25℃) | 150- 190 | 200-300 | 250-450 | 200-400 | 250-450 |
| Melt viscosity (mPa ·s/ 160℃) | 1500-3000 | 2000-4500 | 2000-5000 | 2000-4500 | 3000-8000 |
| Softening point (℃) | 105- 115 | 105- 115 | 100- 110 | 95- 105 | 110- 130 |
| Color (Fe-Co) | ≤ 8 | ≤ 8 | ≤ 8 | ≤ 8 | ≤ 8 |
*4 0% Polyamide Hot Melt Adhesive, 60% Mixed reagent ( Quantity Ratio-- xylene: absolute ethyl alcohol: isopropyl alcohol = 1:1:1 )