Product Details:
|
| Material: | PVA | Diameter: | 2.0+/-0.25dtex |
|---|---|---|---|
| Length(mm): | 3,6, 12mm | Modulus (0.1-0.4%): | 280-300CN/dtex (35Gpa) |
| Tensile Strength: | 11.5CN/dtex Min (1200 Mpa) | ||
| High Light: | 12mm Concrete PP Fiber,6mm Concrete PP Fiber,Custom polyvinyl alcohol fiber |
||
Polyvinyl Alcohol (PVA) Fibre
Performance:
PVA fibers can be easily dissolved like salt in pure water of 20-90 degrees without using any chemical reagent. It has excellentwater solubility and hydrophilicity, especially its moisture absorption rate can reach 5%.In synthetic fiber is relative- ly high,so it is called "synthetic cotton" Its aqueous solution can be biodegrad- ed. It has been used in many fields and has become a functional differential yarn with development prospects.
Packing: 180kgs net per parcel.
Quantity: 12.96mts / 1 x 20GP ; 25.92mts / 1 x 40HQ.
Specification
| Raw material | Polyvinyl Alcohol |
| Diameter | 2.0+/-0.25dtex (15um +3) |
| Tensile strength | 11.5CN/dtex min (1200 Mpa) |
| Break Elongation | 6 - 8% |
| Modulus (0.1-0.4%) | 290+/-10CN/dtex (35Gpa) |
| Resist to hot-water | 98 degree |
| Density | 1.29g/cm3 |
| Length | 6mm, 12mm (as per client`s request) |